Welding Electrode

ROYAL – D2 Mo L (E 309LMo – 16)

AWS : SFA 5.4, E 309LMo - 16

Applications

Suitable for welding steel containing 22 – 26% Cr, 11 – 14 % Ni, 2-3% Mo, also for joints between 18 Cr, – 8 Ni, stainless steel and mild steel, or low alloy steel as well as clad steel.

Welding Positions

1G 2F 3G 4G

Packing

Vaccum packing

Notes On Usage

1) Dry the electrodes at 350°C for 60 minute before use
2) Keep the arc as short as possible.
3) Use currents as low as possible to avoid excessive dilution.

Chemical Composition Of Weld Metal

C%Mn%Si%S%P%Cr%Ni%Mo%
0.040 Max0.50- 2.501.00 Max0.030 Max0.040 Max22.0 – 25.012.0 – 14.02.0 – 3.0

Mechanical Properties Of Weld Metal

U.T.S.(N/mm²)ELONGATION ( L = 4d ) %
520 Min30 % Min

Packing and Welding Current

SIZE ( mm )KG PER PACKETKG PER CARTONCurrent (Amps)In Amps
2.50 X 350210AC/DC (+)45-85
3.15 x 35021085-115
4.00 x 350210100-145
5.00 x 350210135-180

Related Products

1) Redry electrode at 250 °C for 2 hours. Keep the arc as short as possible.
AWS : SFA 5.5, E 7018 B2L EN ISO 3580 A E CrMo 1 L B 32 H5
AWS : SFA 5.5, E 7015 B2L EN ISO 3580 A E CrMo 1 L B 32 H5
AWS : A / SFA 5.11, E Ni Cu - 7 EN ISO 1472 A E Ni 4060